RE: [MW:10577] WELD DETAIL FOR WELDING OF AL 6082-T6

Dear Karthik,
 
I have faced with problem when I tried to weld it before. a HAZ was weak and most times I found a crack in the HAZ. How to avoid it? is any heat treatment required after welding?
 
regards,
Martin.
 

Date: Fri, 1 Apr 2011 09:19:41 +0700
Subject: Re: [MW:10551] WELD DETAIL FOR WELDING OF AL 6082-T6
From: karthik14475@gmail.com
To: materials-welding@googlegroups.com

You can use ER4043

Regards,

(Karthik)

On Thu, Mar 31, 2011 at 6:43 PM, Martin Prad <martin_prad@hotmail.com> wrote:
Dear Friends,
 
Could you please advise some details (welding consumable+elecrtricial detail) for welding of aluminum grade 6082-T6?
Your valuable inputs will be highly appreciated.
 
Thanks,
Martin.

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.


--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.

No comments:

Re: [MW:34832] Inquiry about Single Bevel with Back Grinding

Dear Uday, As per your question that one is called with backing only,Simple both side you are welding it is backing with strip or without st...