[MW:10810] Re: Reg:filler wire for dissimilar material

Hi,

Before suggesting the suitable consumables, you need to mention the
some of the other information like Design temperature & thickness of
base material.

Some of the consumables are not suitable for high temperature service
for e.g 309/309L cannot be used for design temperature more than 315
deg C.

Some general recommendations as mentioned below.

1) P9 to SS310 - ER NiCr-3 (SFA 5.14) or E NiCrFe-2 (SFA 5.11) If the
design temp is more than 538 deg C. (PWHT requirement based on the
base material thickness according to respective design code).

2) P9 to HK40 (centrifugal casting material) - ER NiCr-3 (SFA 5.14) or
E NiCrFe-2 (SFA 5.11). (PWHT requirement based on the base material
thickness according to respective design code).

Hope the above information guide you something.

Cheers!

Raj

On Apr 21, 12:18 pm, venkat kumar <vssl...@gmail.com> wrote:
> dear experts,
> good day all of you.
> i need your valuable help:
> which filler wire we can use for dissimilar metals in heater piping
> 1. ASTM A335 Gr. P9 (9 Cr,1 Mo ) half coupling to ASTM A 240 Gr 310 plate
> fillet weld.
> 2. ASTM A335 Gr. P9 (9Cr, 1 Mo ) coil  to ASTM A 351 Gr.HK 40 plate
>
> PL suggest me
>
> thanks & regards

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.

No comments:

[MW:34820] RE: 34813] Clarification in Rate of heating and cooling.

Hello,   Please see the response below.   Regards.   P. Goswami, P. Eng, IWE.   From: materials-welding@googlegroups.com <materials-weld...