[MW:10667] Re: WELD DETAIL FOR WELDING OF AL 6082-T6

Use:ER 4043(most recommended) or ER 5183(to avoid cracking and to
clear bend test). Generally HAZ of 6082 is weaker than base metal.
There are few PWHT processes available which will solve your problem.
Currently I'm working on aluminum since 9months if you require
anithing more then please let me know.

On Mar 31, 4:43 pm, Martin Prad <martin_p...@hotmail.com> wrote:
> Dear Friends,
>
> Could you please advise some details (welding consumable+elecrtricial detail) for welding of aluminum grade 6082-T6?
> Your valuable inputs will be highly appreciated.
>
> Thanks,
> Martin.                                          

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.